High Quality casting resin, low viscosity, fast curing, SG 2000 L (slow)

The SG 2000 L is a slow version of the SG series casting resin. The SG 2000 L is suitable for making vacuum vacuumform tools and because the heat resistance of 89 degrees Celsius. The SG series and is an HS (high strength) unfilled resin is perfect for making molds and models, test models, first models, prototypes, casting and stamps, mould probes for trimming of prototyping, coping models, negatives, patterns and vacuum forming tools. The SG Series is a 1A: 1B mix ratio casting resin with a work time of 7-8 minutes at room temperature.

The SG 2000 L is a beige product and lends itself well for processing with color pigments or bronze powders. Also the finishing of the cured material is an easy way of post processing.

You can use additives such as color paste, fillers, and powders. The SG 2000L is a polyurethane resin and can have adhesion to much surfaces such as wood, metal, epoxy, polyurethane and more. You can use our Pol-Ease 2300, VL and others to release the material. It can be cast on the most silicone surfaces and moulds as the addition and condensation cured silicone rubbers.

Online Pakckaging: Set 2 kg, Set 10 kg
Packaging: Set 2 kg, Set 10 kg, Set 50 kg, Set 400 kg
Hardness (Shore D): 72 (±3)
Pot life (min.): 7-8
Cure time (uur): 1 – 1,5
Viscosity (cP): 55 ± 5
Density 20°C g/cm3: 1,10
Mixing ratio: 1A:1B by weight (100A:89B bij volume)
Type product: Polyurethaanresin

Flexural strength MPa: 57
Flexural modules MPa : 1500
Flexural strength at break % : 7,5
Compressive strength MPa: 45
Impact resistance °C: 86
Shore hardness Shore D: 72 (±3)
Heat resistent: 86

Application: positives and negative forms, control castings, coping models, vacuum forming tools, mould probes for trimming, prototypes, core boxes, foundry patterns etc.

Downloads

• TDS SG 2000 L